Hi-WAX
Low molecular weight polyolefin

Applications

Pigment dispersant

Uses

Add Hi-WAX and pigment to the three-roll-mill to make up color base.

Availability

It is possible to manufacture high content color masterbatches because Hi-WAX is compatible with pigment and expresses excellent kneading behavior into the higher shear of the extruder.

Recommended grades

PE/PP NL200, NL800
PVC 325MP, 4202E
PS/ABS 1160H

Pigment Dispersant

Pigment Dispersant

Back to Top

Slip agent for PVC

Uses

Add PVC powder, stabilizer, calcium, calcium stearate and Hi-WAX to the twin screw extruder

Availability

It is possible to express excellent slip properties and prevent from degradation of PVC because Hi-WAX affects between the surface of the molder and melting PVC.

Extrusion: Saving power consumption and increasing productivity.
Injection: Improving the appearance of the molding.

Recommended grades

Rigid PVC(Pipes, Fittings),
Soft PVC(Wire & Cable, Sheets):
220MP, 4202E

Slip Agent for PVC

Pigment Dispersant

Back to Top

Release agent for toner

Uses

Add binder resin, pigments, CCA (Charge control agent) and Hi-WAX to the kneader, then pulverize to make up toners.

Availability

It is possible to give anti-offset to a fixing roll because Hi-WAX can be formed wax lubricant film on the fixing roll.

Recommended grades

NP055, NP105, NP505

Release Agent for Toner

Release Agent for Toner

Back to Top

Textile treatment agent

Uses

Disperse Hi-WAX in the hot water to make up wax emulsion. Immerse textiles in the emulsion to attach wax on the surface of the textile, then dry heating.

Availability

It is possible to improve high-speed sewing, tear strength and texture.

Recommended grades

Shrink-proof 4202E, 4051E
Sewing improvement 4051E, 4052E
Texture improvement 2203A

Texrile Treatment Agent

Texrile Treatment Agent

Back to Top

Release agent for injection molding

Uses

Add pellets of ABS, PS , etc. and Hi-WAX to the injection molder.

Availability

It is possible to express excellent releasability and improve the molding cycle and extrusion properties such as die maintenance.

Recommended grades

ABS 200P, 400P, 220MP
PS 1140H

Release Agent for Injection Molding

Release Agent for Injection Molding

Resin / Hi-WAX = 100/0.5